and stepped shaft to 5,5 mm cutting diameter to DIN 9861 standard part 2, type C similar
ISO 9181, type CA
|
Item no.: |
113... | Hardness: | Shaft: | Material HSS |
| The 4th digit of the item no. | and CPM 10 V HRC 62 ± 2 | |||
| indicates the material, see | and Vanadis 23 HRC 64 ± 2 | |||
| How to order | ||||
|
Version: |
Hardened, tempered and fully fine ground | Head: | Material HWS, | |
| finished. Head hot forged and annealed. | HSS, | |||
| In contrast to type CA fine ground finished | CPM 10 V | |||
| with d3 h6 to head. | and Vanadis 23 HRC 50 ± 5 | |||
| Punches made from HWS are temper resistant | ||||
| to 520 °C. | How to order: | For punch type C | ||
| Cutting diameter d1 = 1,7 mm | ||||
|
Materials: |
HWS = High cabon high chrome steel | Shaft diameter d3 = 2,0 mm | ||
| HSS = High speed steel | Total length l1 = 80 mm | |||
| Vanadis 23 = High performance powdered | High carbon high chrome steel | |||
| high speed steel | (HWS): | |||
| CPM 10V = High performance powdered | ||||
| steel | Punch DIN 9861 | |||
|
|
For other materials see | C-HWS 1,7 × 2 × 80 | ||
| (Material Table) | Item no. 1132.17.2.080 | |||
|
d1 h6 |
Gradation |
l1 + 0,5 0 |
d2 |
d3 h6 |
l2 + 0,5 0 |
h + 0,2 0 |
r | |||
| Above | To |
Tolerance |
||||||||
| 0,5 | 1,4 | 0,1 | 71 | 80 | 2,2 | ± 0,05 | 1,5 | 7 | 1,11 |
0,4+0,3 0 |
| 0,5 | 1,9 | 3,0 | ± 0,1 | 2 | 1,37 | |||||
| 1,6 | 2,9 | 4,5 | 3 | 1,80 |
0,6+0,4 0 |
|||||
| 2,5 | 3,5 | 0,5 | 5,5 | 4 | 10 | |||||
| 3,5 | 4,5 | 6,5 | ± 0,2 | 5 | ||||||
| 4,5 | 5,5 | 8,0 | 6 | 2,23 |
1,0+0,5 0 |
|||||